简介：Thermodynamiccalculation,SEM(scanningelectronmicroscopy),TEM(transmissionelectronmicroscopy),XRD(X-raydiffraction),phaseextraction,andchemicalanalysiswereemployedtostudythephasestabilityandphaseprecipitationinanewNi-Cr-Cobasesuperalloyheat-treatedat704and760℃foralongtime.Theresultsshowthattheprecipitatesofthisnewalloyheat-treatedatstandardannealingconditionandheat-treatedat704and760℃foratimeupto2000hareγ′,MC,M23C6,andM6C,andηphaseformsatgrainboundariesandinmatrixofsamplesheat-treatedat760℃aswell.Themassfractionsofγ′(+η),MC,M23C6,andM6Cinallsampleshavenolargechangeswithanincreaseinagingtime,butγ′precipitatesgrowobviously.Theγ′-to-ηtransformationinthesamplesheat-treatedat760℃tookplacewithincreasingagingtime.TheηprecipitatesformaWidmanstattenpattemandtheγ′phaseshaveremeltedpartlyinthesamplesheat-treatedat760℃.Thealloymaintainsabettermicrostructuralstabilityduringprolongedagingat704℃,butaworsemicrostructuralstabilityduringprolongedagingat760℃.

简介：针对23Co14Ni12Cr3Mo超高强度钢材料,研究喷丸强化对其表面性能的影响。采用扫描电镜、白光干涉仪等设备,分析喷丸强化对试样表面形貌、粗糙度、硬度、残余应力、元素含量等的影响。结果表明:喷丸强化后,试样表面留有大量弹坑,产生明显塑性变形;表面粗糙度增大,算术平均粗糙度为1.33μm;硬度显著增大,最表层硬度由喷丸前的HV476增加至HV497,硬化层深度约150μm;试样表层的残余压应力值由375MPa增加至475MPa,最大残余压应力值约518MPa,位于距表面50μm深度处,喷丸形成的残余压应力层深度约为134μm;喷丸后试样中C、Si、Cr等各元素的质量分数均略有增加。喷丸在一定程度上改善了23Co14Ni12Cr3Mo钢材料的表面性能,有利于提高其疲劳抗力和耐腐蚀性。

简介：TheTm-Ni-Coalloyfilmshavebeenpreparedbythesweeppotentialdepositiontechnique.ThesurfaceappearanceofTm-Ni-Coalloyfilmswassilver,smoothandadhesive.ThesurfacesofTm-Ni-Coalloyfilmsobservedbyscanningelectronmicroscope(SEM)wereuniform,adhesiveandcompact.Thesizesofmetallicgrainswereabout80-100nm,100-200amorphousasprovenbytheX-raydiffraction(XRD).

简介：磁性的元素Fe，公司和Ni的线性热扩大(CLE)的系数用与MATLAB计算相结合的理论模型从试验性的信息被估计。模型参数能精确地被决定，并且估计的数据在对试验性的结果的好同意。便于评价，热扩大的理论被使用把CLE分开成它的无磁性、磁性的部件。对CLE的无磁性的贡献的计算基于MnBi/NdFeB混血儿的修改Grc性质结合的磁铁都逐渐地减少，当混合磁铁的密度几乎线性地改善时。在293-398的一个温度范围?K，混合磁铁的coercivity温度系数从0.59逐渐地改善?%比较。建模和频率与二低角落频率认为压力消除阀门是一个秒顺序系统是合理的试验性的结果表演。PID控制，死了的乐队赔偿控制和鷸?鷸？？

简介：2件1Cr17Ni2钢制氮气气瓶使用前经水检、气检和疲劳等试验后发现气瓶瓶体存在漏点。通过宏微观形貌观察、能谱分析、金相检查和硬度测试等手段,结合气瓶的加工及热处理工艺,确定了气瓶裂纹的性质和原因。结果表明：2个气瓶裂纹的性质均为应力腐蚀开裂,建议调整气瓶焊接后的退火温度,降低其应力腐蚀敏感性,并建议对焊接过程进行全方位控制,防止焊接电极接触瓶体等不规范操作行为。

简介：这份报纸在极其细小的颗粒的WC-12%Co合金的磁性、机械的性质上处理codopedVC/Cr3C2和sintering温度的效果。结果证明在最佳的比例的做的VC/Cr3C2的synergistic行动提高坚硬和合金的横向的破裂力量(TRS)，与更多的同类的微观结构。当合金是在1430点的sintered时?C并且与0.5%Cr3C2/0.2%VC，TRS到达3786MPa，坚硬是91.7HRA和比0.6m小的谷物尺寸。谷物生长上的数字分析在sintering过程期间证明在WC谷物边界并且Cr3C2溶解在公司上猛抛的两VC分阶段执行减少固体/液体的界面的精力，溶解和降水的过程极大地被延迟，WC谷物变粗被禁止。

简介：Flexiblethin-filmsupercapacitorswithhighspecificcapacitancearehighlydesirableformodernwearableormicro-sizedelectricalandelectronicapplications.Inthiscontribution,Ni-Cohydroxides(NCH)nanosheetsweredepositedontopofNi-Cualloy(NCA)nanowirearraysformingafreestandingthin-filmcompositeelectrodewithhierarchicalstructureforsupercapacitors.Duringelectrochemicalcycling,thedissolutionofCuintoCuionswillcreatemoreactivesitesonNCA,andtheredepositedcopperoxidecanbecoatedontoNCH,givingrisetosubstantialincreaseinspecificcapacitancewithcycling.Meanwhile,NCAandNCHhaveexcellentconductivity,thusleadingtoexcellentrateperformance.Thisflexiblethin-filmelectrodedeliversanultrahighinitialspecificcapacitanceof0.63F·cm~(-2)(or781.3F·cm~(-3)).Duringcharge-dischargecycles,thespecificcapacitancecanincreaseupto1.18F·cm~(-2)(or1475F·cm~(-3))alongwiththe'self-etching'process.Theelectrodepresentsabetterspecificcapacitanceandratecapabilitycomparedwithpreviouslyreportedflexiblethin-filmelectrode,andthisnoveldesignofetchingtechniquemayexpandtootherbinaryorternarymaterials.

简介：齿轮组件经500h工作后,有1个齿发生了断裂。通过断口宏微观检查、能谱分析,对断裂齿轮的金相组织、化学成分、硬度、表面粗糙度和烧伤情况进行分析,结合对加工方式跟踪,分析结果表明：该齿断裂性质为疲劳断裂,主要与砂轮磨削加工中产生的镶嵌物有关,结合加工生产实际,建议减少磨削进给量,使用合适的冷却液,必要时加以放大镜以及体视显微镜进行检查,尽量避免或减少镶嵌物的产生。

简介：1Cr18Ni9Ti不锈钢球头在焊接后经酸洗，表面存在粗糙的腐蚀凹坑。通过采用S-3700N扫描电子显微镜、能谱分析仪、金相显微镜等对表面粗糙的腐蚀凹坑进行成因分析。结果表明：球头在焊接过程中产生了局部敏化现象，球头的晶粒组织细于与之配合的外套螺母组织，使得球头的耐腐蚀性低于外套螺母，在酸洗去氧化皮的过程中，外套螺母与球头的焊缝区、接管嘴的焊缝区之间形成缝隙，酸洗液中的正负离子移动受到了阻滞，导致缝隙处发生严重腐蚀，最终表现为球头表面的点状腐蚀形貌。定期更换酸洗槽液，降低Cl-浓度，以及在酸洗过程中活动零件，可以减少该类腐蚀的产生。

简介：0Cr18Ni9不锈钢薄壁产品在酸洗过程中易发生过腐蚀。本研究采用0.1mm厚度0Cr18Ni9不锈钢带,对酸洗的各影响因素进行试验研究,结果表明：材料状态不同,耐腐蚀能力不同,退火态更易出现过腐蚀;酸液温度、浓度及酸洗的时间均对不锈钢带腐蚀程度和力学性能有较大影响;在含HF的腐蚀剂中酸洗容易使薄壁不锈钢带力学性能降低,造成材料脆化,且HF含量越高对薄壁不锈钢力学性能影响越大。

简介：采用第一性原理计算揭示了Co掺杂对Ni-Mn-Sn形状记忆合金磁性质的影响。结果表明，掺杂Co使Ni-Mn-Sn合金中两相饱和磁化强度差增大的原因在于其奥氏体的Mn-Mn磁交换作用由反铁磁性转变为铁磁性。奥氏体的顺磁态与铁磁态的能量差对Ni-Co-Mn-Sn的磁转变有重要影响。此外，Co掺杂对磁性的影响与Mn3d态的改变有关。

简介：Theeffectsoflow-CoAB5typehydrogenstoragealloyspreparedbyquenchingandannealingontheperformancesofMH-Nibatterieswereinvestigated,andthecharacteristicsofthelow-CoAB5typehydrogenstoragealloyswerecomparedwiththoseofthehigh-CoAB5typehydrogenstoragealloyaswell.Theresultsshowedthatthefasterthecoolingofthelow-Cohydrogenstoragealloyis,thebetterhomogeneityofthechemicalcompositionforthealloyandthelongercyclelifeofthebatteryare,buttheelectrochemicaldischargecapacityandhigh-ratedischargeabilityarereduced.Thehigh-ratedischargeabilityandchargeretentionofMH-Nibatteriesfortheconventionalas-castannealedlow-Cohydrogenstoragealloyweresuperiortothosefortherapidlyquenchedlow-Cohydrogenstoragealloyandthehigh-Cohydrogenstoragealloy,butalittleinferiorinthecyclelife.

简介：某型号飞机电缆装配前进行例行检查时,发现ZG0Cr14Ni5Mo2Cu上位锁支臂开裂。通过现场调查、对断裂件的材料成分分析、金相组织观察、断口的宏微观观察、硬度检测以及设计结构、受力及现行工艺等综合分析,以确定该上位锁支臂断裂的性质及产生原因。结果表明：上位锁支臂的断裂为过大的装配应力、校形残余应力与氢共同作用下的氢致脆断造成的。此案例分析中发现了隔板设计结构、校形的残余应力问题,为此提出了合理的改进建议。

简介：针对激光直接沉积修复的1Cr15Ni4Mo3N钢零件在磁粉检测时出现的磁痕现象,采用接触通电、湿磁粉连续法,对设计的试样进行磁粉检测,确定磁痕显示位置;利用光学显微镜对磁痕显示处形貌及修复接头和组织进行观察和研究,分析磁痕的性质和形成原因。研究发现:激光直接沉积修复1Cr15Ni4Mo3N钢在磁粉检测过程中与修复区外轮廓完全重合的磁痕显示是伪磁痕显示,主要是由修复区与基体中奥氏体含量的差异造成的。

简介：研究1Cr17Ni2不锈钢中不同δ铁素体相含量变化分别在FeCl3溶液和HNO3＋HF溶液中的耐腐蚀行为。通过腐蚀失重率计算及光学金相显微镜、扫描电子显微镜的观察发现：在FeCl3溶液中,δ铁素体的存在减弱了1Cr17Ni2不锈钢的耐腐蚀性能,δ铁素体是优选腐蚀相;而在HNO3＋HF溶液中,δ铁素体的存在增强1Cr17Ni2不锈钢的耐腐蚀性能,优选腐蚀相则变成了回火索氏体。通过表面腐蚀形貌表征可以实现反推其受到腐蚀介质环境的性质,为1Cr17Ni2不锈钢腐蚀失效与预防提供可行的方法和依据。

简介：激光冲击强化是一种新型表面处理技术,利用高功率激光束冲击金属零件表面,在零件表面形成较大的残余压应力,可有效改善零件的疲劳性能。以发动机1Cr11Ni2W2MoV叶片为研究对象,对其进行了激光冲击强化处理,研究强化处理对材料的微观组织和疲劳性能的影响。研究结果表明：相比未处理试样,激光冲击强化在1Cr11Ni2W2MoV叶片材料表层形成较大的残余压应力,表层晶粒更为细化,叶片的疲劳寿命提高1.7倍。

简介：1Cr15Ni4Mo3N沉淀硬化不锈钢螺栓零件在制造工序磁粉检测时，发现螺栓表面有一条疑似裂纹状线性磁痕显示，后采用荧光渗透检测方法进行辅助检测，原磁痕显示处未见异常荧光显示。结合金相试验分析发现，螺栓原材料内呈带状分布的残余奥氏体，破坏了基体组织和材料磁性的连续性导致出现磁痕显示。研究为该材料在零件制造中磁粉检测的磁痕判定提供了依据。

简介：ThestructureandelectrochemicalcharacteristicsofLa0.7Mg0.3Ni2.875Co0.525Mn0.1-boroncompositewasstudiedsystematically.TheAB3typehydrogenstoragealloysLa0.7Mg0.3Ni2.875Co0.525Mn0.1weresuccessfullysynthesizedbymeansofinter-mediaalloyLa2Mg17.Thealloyswerecompositedwithboronatdifferentweightrate.FromtheXRDanalyses,eachalloyofthisseriesismainlycomposedof(La,Mg)Ni3phaseandtheLaNi5phase,andthephaseabundanceofeachphasevarieswiththeboronweightrate,moreover,aftercomposition,thecandcellvolumesof(La,Mg)Ni3phaseincrease,andtheLaNi5phasekeepthesame,whichindicatethattheboronmayenter(La,Mg)Ni3phase.Theelectrochemicalstudiesshowthatthemaximumdischargecapacityofthecompositesdecreases,butthecyclinglifeimproved.Andthehighratedischargeabilityandexchangeimpendencespectroscopy(EIS)oftheAB3alloysanditscompositewerealsostudied.

简介：采用超音速火焰(HVOF)喷涂制备了一种新型的由纳米、亚微米、微米WC颗粒和CoCr合金组成的多尺度WC-10Co4Cr金属陶瓷涂层，对比了双峰和纳米结构WC-10Co4Cr涂层，在分析了涂层组织的基础上，研究了多尺度涂层的孔隙率、显微硬度、开裂韧性和抗空蚀性能，并分析了多尺度WC-10Co4Cr涂层的空蚀行为和机理。结果表明，HVOF喷涂制备的多尺度WC-10Co4Cr涂层具有≤0.32%的孔隙率和高的开裂韧性，涂层中未发现明显的纳米WC脱碳现象。与双峰与纳米结构涂层相比，多尺度WC-10Co4Cr涂层表现出最优异的抗空蚀性能，在淡水中的抗空蚀性能分别比双峰涂层和纳米结构涂层提高了大约28%和34%。多尺度WC-10Co4Cr涂层的优异抗空蚀性能归结于其独特的微纳米结构和优良的性能，能有效阻碍空蚀裂纹的形成和扩展。

简介：研究结果表明，1Cr18Ni9Ti不锈钢在pH=1的酸性NaCl溶液介质中浸泡最初期，噪声电流曲线无噪声峰，噪声电阻大，电化学阻抗谱为一容抗弧，阻抗模值大，电极表面处于稳定状态。浸泡24h噪声电流曲线出现尖峰波动，但波动峰值只有几个微安，噪声电阻直线下降，阻抗谱高频部分为一容抗弧，低频下出现感抗特征，阻抗模值大幅度下降表面处于点蚀诱导期的亚稳状态。浸泡48h后，噪声电流波动峰值突然增大至100μA，噪声峰也增多，噪声电阻基本稳定，阻抗谱低频下的感抗成分消失，点蚀进入稳定发展阶段。动电位极化曲线与电化学噪声测试结果表明，1Cr18Ni9Ti不锈钢在pH=1的酸性NaCl溶液介质中的耐点蚀性能随浸泡时问延长而降低。