简介：Thermodynamiccalculation,SEM(scanningelectronmicroscopy),TEM(transmissionelectronmicroscopy),XRD(X-raydiffraction),phaseextraction,andchemicalanalysiswereemployedtostudythephasestabilityandphaseprecipitationinanewNi-Cr-Cobasesuperalloyheat-treatedat704and760℃foralongtime.Theresultsshowthattheprecipitatesofthisnewalloyheat-treatedatstandardannealingconditionandheat-treatedat704and760℃foratimeupto2000hareγ′,MC,M23C6,andM6C,andηphaseformsatgrainboundariesandinmatrixofsamplesheat-treatedat760℃aswell.Themassfractionsofγ′(+η),MC,M23C6,andM6Cinallsampleshavenolargechangeswithanincreaseinagingtime,butγ′precipitatesgrowobviously.Theγ′-to-ηtransformationinthesamplesheat-treatedat760℃tookplacewithincreasingagingtime.TheηprecipitatesformaWidmanstattenpattemandtheγ′phaseshaveremeltedpartlyinthesamplesheat-treatedat760℃.Thealloymaintainsabettermicrostructuralstabilityduringprolongedagingat704℃,butaworsemicrostructuralstabilityduringprolongedagingat760℃.

简介：针对23Co14Ni12Cr3Mo超高强度钢材料,研究喷丸强化对其表面性能的影响。采用扫描电镜、白光干涉仪等设备,分析喷丸强化对试样表面形貌、粗糙度、硬度、残余应力、元素含量等的影响。结果表明:喷丸强化后,试样表面留有大量弹坑,产生明显塑性变形;表面粗糙度增大,算术平均粗糙度为1.33μm;硬度显著增大,最表层硬度由喷丸前的HV476增加至HV497,硬化层深度约150μm;试样表层的残余压应力值由375MPa增加至475MPa,最大残余压应力值约518MPa,位于距表面50μm深度处,喷丸形成的残余压应力层深度约为134μm;喷丸后试样中C、Si、Cr等各元素的质量分数均略有增加。喷丸在一定程度上改善了23Co14Ni12Cr3Mo钢材料的表面性能,有利于提高其疲劳抗力和耐腐蚀性。

简介：本文针对N4／1Cr18Ni9Ti与N4／0Cr25Ni20复合板的特殊焊接要求，根据NB／T47014—2011《承压设备焊接工艺评定》的要求，制备2块N4／1Cr18Ni9Ti试板，2块N4I／0Cr25Ni20试板，尺寸均为500mmX150mmX（4＋14）mm。不锈钢基层采用GTAW打底，焊丝选用HOCr21Ni10，SMAW填充与盖面，焊条选用A302与A402。镍复层的焊接采用手工钨极氩弧焊，焊丝选用含Ti、AI等脱氧元素的ERNi-1焊丝，保护气体选择98％Ar＋2％H2。试板焊接完成，外观检验合格后进行100％RT，检测结果符合JB厂r4730，2—2005I级合格，镍复层进行100％PT，检测结果符合JB／T4730．5—2005I级。两种焊接试板分别取样并做拉伸、弯曲力学性能分析，镍复层焊缝做化学成分分析。通过两块焊接试板试验对比，不锈钢基层焊接材料选择HOCr21Ni10焊丝与A302焊条。镍复层焊接采用ERNi-1焊丝，焊接保护气体为98％Ar＋2％H2。通过焊接工艺评定试验研究，解决了N4／1Cr18Ni9Ti与N4I／0Cr25Ni20复合板焊接问题，提高了用户坩埚的返修质量与再次使用寿命，为使用单位节约了成本。

简介：TheTm-Ni-Coalloyfilmshavebeenpreparedbythesweeppotentialdepositiontechnique.ThesurfaceappearanceofTm-Ni-Coalloyfilmswassilver,smoothandadhesive.ThesurfacesofTm-Ni-Coalloyfilmsobservedbyscanningelectronmicroscope(SEM)wereuniform,adhesiveandcompact.Thesizesofmetallicgrainswereabout80-100nm,100-200amorphousasprovenbytheX-raydiffraction(XRD).

简介：磁性的元素Fe，公司和Ni的线性热扩大(CLE)的系数用与MATLAB计算相结合的理论模型从试验性的信息被估计。模型参数能精确地被决定，并且估计的数据在对试验性的结果的好同意。便于评价，热扩大的理论被使用把CLE分开成它的无磁性、磁性的部件。对CLE的无磁性的贡献的计算基于MnBi/NdFeB混血儿的修改Grc性质结合的磁铁都逐渐地减少，当混合磁铁的密度几乎线性地改善时。在293-398的一个温度范围?K，混合磁铁的coercivity温度系数从0.59逐渐地改善?%比较。建模和频率与二低角落频率认为压力消除阀门是一个秒顺序系统是合理的试验性的结果表演。PID控制，死了的乐队赔偿控制和鷸?鷸？？

简介：本文描述了目前国内NiMnCo片状触媒的生产状况，研究探索了影响片状触媒自动化生产的因素，并通过改进生产工艺，利用现代化设备等方法，使NiMnCo片状触媒生产效率和产品质量大幅提高。

简介：0Cr17Ni4Cu4Nb为我厂最新引进的材料．该钢具有良好的耐腐蚀性，耐蚀性优于一般马氏体不锈钢，与一般奥氏体不锈钢相似。它具有良好的切削性能，不需预热就可以焊接并且焊后可不进行局部退火。它主要用于制造耐蚀和高强度部件如喷气发动机压气机机匣及大型汽轮机末级叶片。

简介：TiC/Cr18Ni8steelbondedcarbidesweresynthesizedbyvacuumsinteringwithmixedpowdersofiron,ferrotitanium,ferrochromium,colloidalgraphiteandnickelasrawmaterials.Themicrostructureandmicrohardnessofthesteelbondedcarbideswereanalyzedbyscanningelectronmicroscope(SEM),X-raydiffraction(XRD)andRockwellhardometer.ResultsshowthatthephasesofsteelbondedcarbidesmainlyconsistofTiCandFe-Cr-Nisolidsolution.ThesynthesizedTiCparticlesarefine.Mostofthemarenotmorethan1μm.Withtheincreaseofsinteringtemperature,theporosityofTiC/Cr18Ni8steelbondedcarbidesdecreasesandthedensityandhardnessincrease,butthesizeofTiCparticlesslightlyincreases.Underthesamesinteringconditions,thedensityandhardnessofsteelbondedcarbideswithC/Tiatomicratio0.9arehigherthanthosewithC/Tiatomicratio1.0.TheTiCparticleswithC/Tiatomicratio0.9aremuchfinerandmorehomogeneous.

简介：Theeffectofnonmetallicinclusionsinthedropletofthestainlesssteelcoveredelectrodeontheporositywasresearched.Theresultshowsthatthenonmetallicinclusionsinthedropletarespherical,theircompositionisdifferentfromtheoneofslagandtheinclusionshavethecharacterof"innerformation".Whentheratioofrutiletoilmeniteinthecoatedmaterialisincreased,thedropletbecomescoarse,thecontentofnonmetallicinclusioninthedropletdecreases,andtheporositysensitivityintheweldmetalalsodecreases.Whentheratiooffledspartoilmeniteinthecoatedmaterialisincreased,thedropletbecomesfine,thecontentofnonmetallicinclusioninthedropletincreases,andtheporositysensitivityintheweldmetalincreases.WhentheratioofFe2O3toilmeniteinthecoatedmaterialisincreased,thedropletbecomesfine,thecontentofnonmetallicinclusiondecreases,whiletheporositysensitivitydoesnotreduce.

简介：本文采用真空钎焊工艺对1Cr18Ni9Ti不锈钢进行了焊接,焊后通过扫描电镜、电子探针扫描、XRD等分析测试手段对试样进行分析研究。研究结果表明:试样表面生成了碳化物,为TiC和Ti8C5;表面碳化物的生成过程是在真空高温环境下,Ti元素与环管中向外扩散的C发生固相扩散反应生成TiC,过量的Ti再与TiC反应生成Ti8C5。

简介：2件1Cr17Ni2钢制氮气气瓶使用前经水检、气检和疲劳等试验后发现气瓶瓶体存在漏点。通过宏微观形貌观察、能谱分析、金相检查和硬度测试等手段,结合气瓶的加工及热处理工艺,确定了气瓶裂纹的性质和原因。结果表明：2个气瓶裂纹的性质均为应力腐蚀开裂,建议调整气瓶焊接后的退火温度,降低其应力腐蚀敏感性,并建议对焊接过程进行全方位控制,防止焊接电极接触瓶体等不规范操作行为。

简介：本文从观测常规产品Ni70Mn25Co5触媒合金片的表面缺陷入手，讨论了触媒片表观质量对金刚石合成效果的影响，从而也为触媒产品质量标准的制定提供了某些参考依据。

简介：

简介：这份报纸在极其细小的颗粒的WC-12%Co合金的磁性、机械的性质上处理codopedVC/Cr3C2和sintering温度的效果。结果证明在最佳的比例的做的VC/Cr3C2的synergistic行动提高坚硬和合金的横向的破裂力量(TRS)，与更多的同类的微观结构。当合金是在1430点的sintered时?C并且与0.5%Cr3C2/0.2%VC，TRS到达3786MPa，坚硬是91.7HRA和比0.6m小的谷物尺寸。谷物生长上的数字分析在sintering过程期间证明在WC谷物边界并且Cr3C2溶解在公司上猛抛的两VC分阶段执行减少固体/液体的界面的精力，溶解和降水的过程极大地被延迟，WC谷物变粗被禁止。

简介：Flexiblethin-filmsupercapacitorswithhighspecificcapacitancearehighlydesirableformodernwearableormicro-sizedelectricalandelectronicapplications.Inthiscontribution,Ni-Cohydroxides(NCH)nanosheetsweredepositedontopofNi-Cualloy(NCA)nanowirearraysformingafreestandingthin-filmcompositeelectrodewithhierarchicalstructureforsupercapacitors.Duringelectrochemicalcycling,thedissolutionofCuintoCuionswillcreatemoreactivesitesonNCA,andtheredepositedcopperoxidecanbecoatedontoNCH,givingrisetosubstantialincreaseinspecificcapacitancewithcycling.Meanwhile,NCAandNCHhaveexcellentconductivity,thusleadingtoexcellentrateperformance.Thisflexiblethin-filmelectrodedeliversanultrahighinitialspecificcapacitanceof0.63F·cm~(-2)(or781.3F·cm~(-3)).Duringcharge-dischargecycles,thespecificcapacitancecanincreaseupto1.18F·cm~(-2)(or1475F·cm~(-3))alongwiththe'self-etching'process.Theelectrodepresentsabetterspecificcapacitanceandratecapabilitycomparedwithpreviouslyreportedflexiblethin-filmelectrode,andthisnoveldesignofetchingtechniquemayexpandtootherbinaryorternarymaterials.

简介：

简介：齿轮组件经500h工作后,有1个齿发生了断裂。通过断口宏微观检查、能谱分析,对断裂齿轮的金相组织、化学成分、硬度、表面粗糙度和烧伤情况进行分析,结合对加工方式跟踪,分析结果表明：该齿断裂性质为疲劳断裂,主要与砂轮磨削加工中产生的镶嵌物有关,结合加工生产实际,建议减少磨削进给量,使用合适的冷却液,必要时加以放大镜以及体视显微镜进行检查,尽量避免或减少镶嵌物的产生。

简介：1Cr18Ni9Ti不锈钢球头在焊接后经酸洗，表面存在粗糙的腐蚀凹坑。通过采用S-3700N扫描电子显微镜、能谱分析仪、金相显微镜等对表面粗糙的腐蚀凹坑进行成因分析。结果表明：球头在焊接过程中产生了局部敏化现象，球头的晶粒组织细于与之配合的外套螺母组织，使得球头的耐腐蚀性低于外套螺母，在酸洗去氧化皮的过程中，外套螺母与球头的焊缝区、接管嘴的焊缝区之间形成缝隙，酸洗液中的正负离子移动受到了阻滞，导致缝隙处发生严重腐蚀，最终表现为球头表面的点状腐蚀形貌。定期更换酸洗槽液，降低Cl-浓度，以及在酸洗过程中活动零件，可以减少该类腐蚀的产生。

简介：0Cr18Ni9不锈钢薄壁产品在酸洗过程中易发生过腐蚀。本研究采用0.1mm厚度0Cr18Ni9不锈钢带,对酸洗的各影响因素进行试验研究,结果表明：材料状态不同,耐腐蚀能力不同,退火态更易出现过腐蚀;酸液温度、浓度及酸洗的时间均对不锈钢带腐蚀程度和力学性能有较大影响;在含HF的腐蚀剂中酸洗容易使薄壁不锈钢带力学性能降低,造成材料脆化,且HF含量越高对薄壁不锈钢力学性能影响越大。

简介：采用第一性原理计算揭示了Co掺杂对Ni-Mn-Sn形状记忆合金磁性质的影响。结果表明，掺杂Co使Ni-Mn-Sn合金中两相饱和磁化强度差增大的原因在于其奥氏体的Mn-Mn磁交换作用由反铁磁性转变为铁磁性。奥氏体的顺磁态与铁磁态的能量差对Ni-Co-Mn-Sn的磁转变有重要影响。此外，Co掺杂对磁性的影响与Mn3d态的改变有关。