简介：SomenewNi-saving25Crduplexstainlesssteels(DSS)havebeendeveloped.Theresultsindicatethatthealloyhasabalancedferrite-austeniterelationafterhotforgeandsolidsolutiontreatmentat1000℃.TheelementsWandCuhaveamarkedeffectonthemicrostructureofthealloy.ThepittingpotentialofthesteeladdingWandCuelementsreachesthemaximumvalueof435mV.Thetensilestrengthandpercentageofareareductionofallsteelsinthispaperare800-900MPaand60%-70%,respectively.Thetensileelongationsofthealloysareallabove30%.Theexperimentalsteelshavegoodcorrosionandmechanicalproperty.

简介：CuprecipitationbehaviorsintwoCu-bearingausteniticantibacterialstainlesssteels,type304andtype317L,weresystematicallystudiedbyusingrelativelysimplemethodsformaterialsanalysis,includingmicro-hardness,electricalresistivity,electrochemicalimpedancespectroscopy,X-raydiffractionanddifferentialscanningcalorimetry.Theresultsindicatedthatafteragingatelevatedtemperature,themicro-hardness,electricalresistivity,electrochemicalimpedanceandlatticeconstantofthesteelwereallvariedatdifferentdegreesduetotheprecipitationandgrowthofCu-richphases.TheresultsalsoshowedthattheheatevolutionduringtheprocessofCuprecipitationcouldbesensitivelydetectedbymeansofdifferentialscanningcalorimetry,obtainningthestartingtemperature,peaktemperature,peakareaoftheCu-richprecipitation,andeventheactivationenergybycalculation.TheresultsconfirmedthattheCu-richphasedprecipitationintheCu-bearingausteniticantibacterialstainlesssteelshouldbeathermalactivationprocesscontrolledbyCudiffusion.AllthematerialsanalysismethodsusedinthisstudycanbemoresimpleandeffectiveforapplicationinR&DoftheCu-bearingantibacterialstainlesssteels.