简介：如歌的岁月,荏苒的时光。《资源再生》杂志喜迎200期之际,我们非常荣幸地收到位行业领导、专家及企业家等众多朋友为本刊发来的寄语,其中饱含对我们的鼓励、深深的厚爱和热忱的关心与殷切期望。这是教诲也是鞭策,我们将以此作为继续的目标和方向,披荆斩棘、砥砺前行。200期只是弹指一挥间,我们期待下一个200期,因为您的参与,它将更加精彩!

简介：ThedosimetricphosphorsLi_3PO_4:M(M=Tb,Cu)wereproducedbymodifiedsolid-statemethod.ThestructuralandmorphologicalcharacterizationwascarriedoutthroughX-raydiffraction(XRD)andscanningelectronmicroscope(SEM).Additionally,thephotoluminescence(PL),thermoluminescence(TL)andopticallystimulatedluminescence(OSL)propertiesofpowderLi_3PO_4dopedwithTbandCuwerestudied.ItisadvocatedthatLi_3PO_4:CuphosphornotonlyshowshigherOSLsensitivity(25timesormore)butalsogivesfasterdecayinOSLsignalsthanthatofLi_3PO_4:Tb~(3+)phosphor.Theminimumdetectabledose(MDD)ofLi_3PO_4:M(M=Tb,Cu)phosphorsisfoundtobe21.69×10~(-3)and3.33×10~(-6)J·kg~(-1),respectively.InOSLmode,phosphorshowslineardoseresponseintherangeof0.02-20.00J·kg~(-1).InTLmode,sensitivityofLi_3PO_4:CuphosphorismorethanthatofLi_3PO_4:Tbphosphor.Thekineticsparameterssuchasactivationenergyandfrequencyfactorsweredeterminedbypeakshapemethod,andphotoionizationcrosssectionsofpreparedphosphorwerecalculated.

简介：FluorescenceandcofluorescencepropertiesofTb(Ⅲ)solidcomplexeswerestudiedusingpyromelliticacid(PMA)asligandandfluorescenceinertionsasdopingelements.Thecofluorescenceenhancement,aresultofligandsensitizedfluorescence,wasobservedinTb(Ⅲ)solidcomplexesdopedwithfluorescentinertionsLa(Ⅲ),Gd(Ⅲ),Ca(Ⅲ),andSr(Ⅲ).Theeffectofthetypeandcontentofdopingelementsonfluorescenceenhancementwasstudied,andoptimumconditionsweredetermined.TheresultsshowthatGd(La,Ca,Sr)hasclearcofluorescenceeffectinsolidcomplexTb-M-PMAsystem,andinpresentwork,rareearthcomplexfluorescentpowderthatemitsbrightgreenfluorescenceatultravioletexcitationwasobtained,whichhadpotentialapplicationasfluorescentanti-counterfeitink.

简介：由七0四厂弋陕西华电材料科技有限公司）研究所承担研制的“HBT-200固态脉冲形成线”项目是为用户单位研制的新型储能器材。该项目利用高介电常数陶瓷聚合物复合材料作为储能介质制作脉冲形成线，具有储能密度高、无泄漏，可简化系统结构等特点。该项目的创新开发了一种介质均匀、

简介：Basedonclustervariationmethod(CVM)andnaturaliterationmethod(NIM),order-disorderphasetransitionintheintercalationcompoundsM1/2TiS2issimulatedbycomputer.Thefavorableconditions,underwhich3a0×a0superstructureisformed,aregiven,andtheresultsareingoodagreementwiththeexperimentsandtheoreticalcalculations.TherelationshipbetweencriticaltemperatureandM-ion-vacancyinteractionparameterislinear.

简介：InordertoimprovetheelectrochemicalcyclestabilityofLa-Mg-Nisystem(PuNi3-type)hydrogenstoragealloy,NiinthealloyswaspartiallysubstitutedbyM(M=Cu,Al,Mn).AnewLa-Mg-NisystemelectrodealloysLa0.7Mg0.3Ni2.55-xCo0.45Mx(M=Cu,Al,Mn;x=0,0.1)werepreparedbycastingandrapidquenching.Theeffectsofelementsubstitutionandrapidquenchingonthemicrostructuresandelectrochemicalperformancesofthealloyswereinvestigated.TheresultsbyXRD,SEMandTEMshowthatthealloyshaveamultiphasestructure,includingthe(La,Mg)Ni3phase,theLaNi5phaseandtheLaNi2phase.Therapidquenchingandelementsubstitutionhaveanimperceptibleinfluenceonthephasecompositionsofthealloys,butbothchangethephaseabundanceofthealloys.Therapidquenchingsignificantlyimprovesthecompositionhomogeneityofthealloysandmarkedlydecreasesthegrainsizeofthealloys.TheCusubstitutionpromotestheformationofanamorphousphaseintheas-quenchedalloy,andareversalresultbytheAlsubstitution.Theelectrochemicalmeasurementindicatesthattheelementsubstitutiondecreasesthedischargecapacityofthealloys,whereasitobviouslyimprovesthecyclestabilityofthealloys.ThepositiveinfluenceofelementsubstitutiononthecyclelifeofthealloysisinsequenceAl＞Cu＞Mn,andnegativeinfluenceonthedischargecapacityisinsequenceAl＞Mn＞Cu.Therapidquenchingsignificantlyenhancesthecyclestabilityofthealloys,butitleadstoadifferentextentdecreaseofthedischargecapacityofthealloys.

简介：对多次电镀铬的300M钢试样的疲劳性能、氢脆倾向、疲劳断口进行了测试和分析，以研究镀铬次数、镀铬层厚度对300M钢疲劳性能的影响规律。结果表明：镀铬层对300M钢的疲劳性能影响很大，在试验条件下，带镀层试样较未电镀试样的疲劳强度和相同应力条件下的疲劳寿命降低约60％，且镀层越厚疲劳寿命越低；这种影响与电镀次数无明显关系，只要执行正常的除氢工艺，重复电镀多达15次的300M钢仍未发现氢脆倾向。断口分析表明：疲劳裂纹主要起源于镀铬层或镀层与基体的界面处，疲劳性能的大幅降低主要与镀铬层本身的特性有关。

简介：针对AM60B合金在环境温度25～200℃、载荷12.5～300N的条件下进行干摩擦磨损实验。结果表明：随着载荷的增大,磨损率增加;从轻微磨损到严重磨损的转变的临界载荷分别为25℃时275N,100℃时150N,200℃时75N。在低载荷（〈50N）下,200℃下的磨损率低于25℃和100℃的。在轻微磨损阶段,磨损机制为磨粒磨损、氧化磨损和剥层磨损。当轻微磨损到严重磨损的转变开始时,剥层磨损发挥主要作用,剥层磨损是从基体内部发生的剥落。随后,塑性挤出磨损作为严重磨损出现,同时伴随着从轻微磨损到严重磨损的转变。厚的、硬的摩擦层通过限制磨面的塑性变形来阻碍从轻微磨损到严重磨损的转变。

简介：河南豫光金铅集团公司在2014年度表彰大会上，总结2014年成绩，规划新一年的工作方向，大会披露2014年豫光金铅集团销售收入和工业总产值历史上首次双双突破200亿元。2014年在铅行业整体亏损，整个电解锌行业大面积亏损的情况下，豫光铅、锌系统都实现盈利；豫光有史以来投资最大的项目冶炼渣处理技术改造项目也顺利拉通，自主研发的世界首条双底吹工艺成功运用到生产实践中，试产一次性取得成功，企业多元化产业、循环经济以及生产经营等各个环节都取得了可喜的成绩。

简介：超华科技（002288）2月20日晚间公告，根据《广东省著名商标认定和管理规定》和《广东省工商行政管理局关于广东省著名商标认定和管理的实施细则》的规定，经广东省著名商标评审委员会评审通过，公司“M”商标被延续认定为“广东省著名商标”，认定商品为“覆铜箔层压酚醛树脂板（绝缘材料）”，有效期自2013年3月24日起至2016年3月23日止。

简介：本文对比分析了氮基保护气氛和真空两种热处理加热介质对300M钢疲劳性能的影响，并研究了热处理后表面喷丸强化对300M钢疲劳性能的改善情况。结果表明，由于氮基保护气氛热处理后表面层有一定程度的氧化脱碳，故钢的疲劳极限比真空热处理的低近30％；由于喷丸强化后表面形成较大的压应力，消除了表面氧化层等不良影响，氮基保护气氛热处理后经喷丸的300M钢疲劳极限比未喷丸的提高约40％。