ThemagnesiabasedcurablespecimenswithdifferentSi3N4contentswerecastedusingsinteredmagnesite(w(MgO)=95%)asstartingmaterial,SiO2micro-powderasbinder,0.3%,4%and5%β-Si3N4powderreplacingtheequaladditionofmagnesiapowderrespectively.Theslagresistancetestwascarriedoutat1550℃for3husingBaosteeltundishslagandstaticcruciblemethod.Theresultindicatesthat:introducingSi3N4couldobviouslyimprovetheslagresistanceofMgObasedcastable,whichincreasedwithincreasingSi3N4.DenseSiO2sinteredlayerformedonthesurfaceofmagnesiabasedcastablebecauseoftheoxidationofSi3N4addition,whichcanpreventthefurtherslagpenetration.Inthedeepinnerofcastable,thepartial-pressureofoxygenwasverylow,soSi3N4canexiststably.Meanwhileinreducingatmosphere,Si3N4washardtobesintered,whichresultedinthelooseinteriorstructureofMgObasedcastable.