ThesusceptibilityofweldedjointfortheX65pipelinesteeltoH2Sstresscorrosioncracking(SCC)isinvestigated.SCCtestsonthesteelarecarriedoutintheenvironmentbasedonNACETM-01-77solutionwithsaturatedgaseousH2S.Thethresholdstressintensityfactorandcrackpropagationvelocityarecalculatedaccordingtowedge-openingloading(WOL)specimens.Thethree-dimensionalelastic-plasticfiniteelementanalysisofWOLspecimensisperformedbyusingtheFEMprogrammingpackageANSYS.Stressfieldandconcentrationofhydrogendistributionpropertyaheadofthecracktipareobtained.ThispapersurveyedthemicrostructureofweldedjointandstudiedonthemechanicalpropertiesofX65pipelinesteel.Itprovidesexperimentalbasisforstudyingstresscorrosion.Theresultsofnumericalanalysisareconsistentwithconclusionsofstresscorrosiontest.